Investigation of plasticizer evaporation of local electrical cable insulations

Abstract

Though insulation is critical to the performance of an electrical cable the assessment of the status of an insulation is still a major challenge. Since the root cause of most electrical cable failures is due to insulation deterioration, if the rate of aging can be predicted, properly scheduled, appropriate maintenance programs can nearly eliminate cable failures. The kinetics of plasticizer evaporation of polyvinyl chloride based locally manufactured electrical cable insulations were investigated. Plasticizer evaporation is a slow process under low temperatures and would take years to study under such conditions. Therefore, accelerated conditions were used to get readings within the limited timeframe. Nevertheless, data obtained under accelerated conditions was mapped to normal conditions through Arrhenius approach. Deconvoluted derivative thermograms were used to identify the initial plasticizer percentages and Arrhenius approach was used to map accelerated condition measurements to ambient temperature evaporation rates.